Multicore 7mm Stick Lead Free Solder, +227°C Melting Point

  • RS-stocknr. 512-5801
  • Fabrikantnummer 761345
  • Fabrikant Multicore
Datasheets
Wetgeving en compliance
Conform
Land van herkomst: GB
Productomschrijving

99C Lead-free Solder Stick

High purity extruded solder alloy containing 99.3% tin & 0.7% copper, suitable for solder baths or pots.

Less dross on initial melting
More solder joints weight for weight
Improved wetting of electronic components & PCBs
Melts at 227°C
Stick weight 80 g Diameter is 7,05 mm

Lead Free Stick Solder

Specificaties
Kenmerk Waarde
Wire Diameter 7mm
Percent Lead 0%
Product Form Stick
Melting Point 227°C
Percent Tin 99.3%
Product Weight 80g
Flux Content Percent 0%
Percent Copper 0.7%
5 op voorraad - levertijd is 1 werkdag(en) (EU-voorraad)
655 op voorraad - levertijd is 2 werkdag(en) (UK-voorraad)
Prijs Each (In a Pack of 5)
11,516
(excl. BTW)
13,934
(incl. BTW)
Aantal stuks
Per stuk
Per pak*
5 +
€ 11,516
€ 57,58
*prijsindicatie
Related Products
No-clean solder wire (RT15) and activated no-clean solder ...
Description:
No-clean solder wire (RT15) and activated no-clean solder wire (A11).A11 spools are designed for soldering connectors to all substrates.RT15 spools with fast wetting are suitable for SMD repairs.
Sn60Pb40 soldering wire with 1 % halogen-free active ...
Description:
Sn60Pb40 soldering wire with 1 % halogen-free active flux core F-SW 34, No CleanFor use in electronic engineering, especially in SMD technologySolid at 183 °C, liquid at 190 °C.
Soldering wire with 5 halogen-free activated colophony cores3.5% ...
Description:
Soldering wire with 5 halogen-free activated colophony cores3.5% flux 1.1.3B, in accordance with DIN EN 29454 Part 1.
The Trilence flux system has been designed for ...
Description:
The Trilence flux system has been designed for demanding soldering tasks in automated soldering processes. Due to its optimised properties, the flux system is also suitable for manual soldering and rework. The Trilence flux system has been designed for demanding ...