Felder Lottechnik 1mm Wire Solder, +183°C Melting Point

Datasheets
Wetgeving en compliance
Niet conform
Land van herkomst: DE
Productomschrijving

Solder, Felder ELR DIN 8516, F-SW34

Sn60Pb40 soldering wire with 1 % halogen-free active flux core F-SW 34, No Clean
For use in electronic engineering, especially in SMD technology
Solid at 183 °C, liquid at 190 °C.

Standards

DIN 8516

Specificaties
Kenmerk Waarde
Wire Diameter 1mm
Percent Lead 40%
Product Form Wire
Melting Point +183°C
Percent Silver 0%
Percent Tin 60%
Flux Type Rosin Based
Product Weight 1kg
Flux Content Percent 1%
Percent Copper 0%
9 op voorraad - levertijd is 1 werkdag(en)
Prijs Each
48,42
(excl. BTW)
58,59
(incl. BTW)
Aantal stuks
Per stuk
1 - 9
€ 48,42
10 - 19
€ 46,48
20 - 49
€ 45,03
50 +
€ 41,16
Related Products
No-clean solder wire (RT15) and activated no-clean solder ...
Description:
No-clean solder wire (RT15) and activated no-clean solder wire (A11).A11 spools are designed for soldering connectors to all substrates.RT15 spools with fast wetting are suitable for SMD repairs.
RA soldering wire with 5 activated colophony cores ...
Description:
RA soldering wire with 5 activated colophony cores with 2.5% F-SW 26 fluxOutstanding wetting and spreading properties, also suitable for difficult solders in electrical engineering and electronicsHigh-purity alloys for reliable solder joints.
Stannol Kristall solder wires have been specially formulated ...
Description:
Stannol Kristall solder wires have been specially formulated to complement No Clean wave and reflow soldering processes. They are also applicable to repair operations carried out after a cleaning process, eliminating the need for further cleaning. Stannol Kristall solder wires ...
5-core Crystal 511 solder wire comprising a balance ...
Description:
5-core Crystal 511 solder wire comprising a balance of resins and activators to ensure maximum activity and leave only small quantities of clear residue.This 511 flux effectively brazes bare copper, brass, nickel, tin / lead finishes as well as oxidised ...